The surface material of Gongli ASA Spanish Roof Sheet is an imported ultra-high weather-resistant engineering resin, which has extraordinary weather resistance and can maintain its color stability.
Gongli ASA spanish roof sheet has super weather resistance and anti-corrosion performance. ASA Spanish roof sheet is soaked in salt, alkali and various acids below 60% for 24 hours without chemical reaction. ASA spanish roof sheet is the preferred plastic roof sheet material for chemical industry areas and acid rain areas.
GONGLI ASA Spanish roof panel itself is dense and does not absorb water, and there is no microporous water seepage. ASA Spanish roof sheet is a one-piece roof tile design, and there are few overlapping positions during installation. Under the condition of correct installation, the waterproof performance of ASA Spanish 1050 roof sheet can be maximized.
Gongli ASA Spanish 1050 roof sheet is an insulation roofing material product, and will remain intact in case of accidental discharge or thunderstorms.
Gongli ASA Spanish 1050 roof sheet material belongs to flame-retardant material, which will be extinguished when it leaves the fire.
Width: 1050mm
Effecived width: 960mm
Length: Customized
Thickness: 2.3mm, 2.5mm, 3.0mm
Application: Residential, Villas, Resorts, Hotels, Government Projects, etc.
ASA Spanish roof sheet is one of the most popular profiles in the Gongli product line, prized for its simple one-piece design, which exhibits a unique corrugated pattern on the roof surface. Compared to clay roof tiles, Spanish colonial roof sheet can enhance almost any architectural style.
The ASA Spanish roof sheet has been praised for its simple one-piece design, which combines a unique corrugated pattern on the roof while reducing the risk of water leaks by reducing tile overlapping locations.
ASA Spain 1050 Roof Sheets are available in custom finishes, matt, glossy and inkjet finishes.
Gogonli ASA Spanish roof panels provide retro European architectural style for any building, and are commonly used in the roofing of self-occupied residences, villas, hotels, resorts and other buildings.
NO. | Test Item | Test Method | Test Condition | Test Result | |
1 | Xenon-arc Exposure | ISO 4892-2:2013,ISO 105-A02:1993 | ISO 4892-2:2013 cycle 4 Irradiance:(0.51±0.02)W/(m2·nm)@340nm 102min light at (63±3)℃BPT,(50±10)℃RH | Greyscale | 2-3 |
∆E*ab | 3.5 | ||||
2 | Thermal resistance | With reference to ASTM D3045-92(2010) and client’s requirements | 150℃.30min | Visible deformation and color fading, but o other visible change. | |
3 | Muriatic acid resistance | With reference to ISO 175-2010 and client’s requirements | Medium: 35%(m/m) HCI(AR) | No visisble change | |
4 | Sulfuric acid resistance | With reference to ISO 175-2010 and client’s requirements | Medium: 30%(m/m) H2SO4(AR) | No visisble change | |
5 | Alikali resistance | With reference to ISO 175-2010 and client’s requirements | Medium: 40% (m/m) NaOH(AR) | No visible change. | |
6 | Density | ISO 1183-1:2012 Method A | Abosolute alcohol, 23±0.5℃ | 1.799g/cm3 | |
7 | Flexural strength | ISO 178:2010/Amd.1:2013 | Specimen:100×10.96×3.12mm | 41.3MPa | |
8 | Flexural modulus | 4520MPa | |||
9 | Charpy unnotched impact strength | ISO 179-1: 2010 | Specimen: ISO 179-1/1Eu | 38Kj/M2 | |
10 | Vicat softening temperature | ISO 306:2004 Method B50 | Specimen thickness: 3.01mm | 77.3℃ | |
11 | Tensile strength | ISO 527-1:2012 and ISO 527-2:2012 | Specimen: Type 1B | 20.3MPa | |
12 | Nominal tensile strain at break | 13% | |||
13 | Impact resistance | GB/T 8814-2004 Section 5.7 and 6.7 | Precondition:-10℃,1h→ | Number of spcimen breakage:0 | |
14 | Dimensional change | With reference to ASTM D1204-08 and client’s requirement | Condition: 100℃,60min→ | X | -0.7% |
Y | -1.3% | ||||
15 | Oxygen Index | ISO 4589-1: 1996 and ISO 4589-2: 1996/Amd.1:2005 | Specimen: Type III | 32.8% | |
16 | Horizontal burning test | UL 94-2013 Section 7 | Specimen: 126×13.4×3.0mm | HB | |
17 | 20mm Vertiacal burning test | UL 94-2013 Section 8 | Specimen: 126×13.4×3.0mm | V-1 | |
18 | Burning test | DIN 4102-1:1998-05 | See appendix1 | The sample tested met the requirements of class B2 |