  • ASA Spanish PVC roof sheet accessories endcap of the main ridge tile

ASA Spanish PVC roof sheet accessories endcap of the main ridge tile

Brand: Gongli
Model: XR-C1130
Layers: 4 Layers
Supply Type: OEM/ODM
Warranty: 15 Years
Delivery Time:10-15 Working days after advance
Share:
SPANISH ROOF SHEET ACCESSORIES

ASAPVC Color

8

Product Details

Width: 1050mm

Effecived width: 960mm

Length: Customized

Thickness: 2.3mm, 2.5mm, 3.0mm

Application: Residential, Villas, Resorts, Hotels, Government Projects, etc.

Product Application Range
ASA Spanish PVC roof sheet Test Technical Data From SGS

 

NO.

Test Item

Test Method

Test Condition

Test Result

1

Xenon-arc Exposure

ISO 4892-2:2013,ISO 105-A02:1993  
Cor2: 2005 and ASTM D2244-11

ISO 4892-2:2013 cycle 4 Irradiance:(0.51±0.02)W/(m2·nm)@340nm 102min light at (63±3)℃BPT,(50±10)℃RH
18min light and water sparay Filter: Boro/Boro
Exposure period: 500h

Greyscale

2-3

∆E*ab

3.5

2

Thermal resistance

With reference to ASTM D3045-92(2010) and client’s requirements

150℃.30min

Visible deformation and color fading, but o other visible change.

3

Muriatic acid resistance

With reference to ISO 175-2010 and client’s requirements

Medium: 35%(m/m) HCI(AR)
Method: Immersion method
Temperature: Room temperature
Test time: 48h

No visisble change

4

Sulfuric acid resistance

With reference to ISO 175-2010 and client’s requirements

Medium: 30%(m/m) H2SO4(AR)
Method: Immersion method
Temperature: Room temperature
Test time: 48h 

No visisble change

5

Alikali resistance

With reference to ISO 175-2010 and client’s requirements

Medium: 40% (m/m) NaOH(AR)
Method: Immersion method
Temperature: Room temperature
Test time: 48h

No visible change.

6

Density

ISO 1183-1:2012     Method A

Abosolute alcohol, 23±0.5℃

1.799g/cm3

7

Flexural strength

ISO 178:2010/Amd.1:2013
Method A

Specimen:100×10.96×3.12mm
Testing speed: 1mm/min
Span: 50mm

41.3MPa

8

Flexural modulus

4520MPa

9

Charpy unnotched impact strength

ISO 179-1: 2010

Specimen: ISO 179-1/1Eu
Specimen thickness:3.13mm
The capcaity of the pendulum: 5J
Impact speed: 2.90m/s
Span: 62mm

38Kj/M2
C(complete break)

10

Vicat softening temperature

ISO 306:2004 Method B50

Specimen thickness: 3.01mm
Rate of temperature: 50℃/h

77.3℃

11

Tensile strength

ISO 527-1:2012 and ISO 527-2:2012

Specimen: Type 1B
Specimen thickness:3.05mm
Testing speed: 5mm/min
Grip separation:115mm

20.3MPa

12

Nominal tensile strain at break

13%

13

Impact resistance

GB/T 8814-2004 Section 5.7 and 6.7

Precondition:-10℃,1h→
Take out and do test within 10s.
Specimen thickness:3.02mm
Geometry: H.25
Strike weight: 1.0kg
Span: 200mm
Number of specimens tested:10

Number of spcimen breakage:0

14

Dimensional change

With reference to ASTM D1204-08 and client’s requirement

Condition: 100℃,60min→
23±2℃,50±5%RH,1h
Specimen: 25x25cm
Medium:Talcum powder

X
drection

-0.7%

Y
direction

-1.3%

15

Oxygen Index

ISO 4589-1: 1996 and ISO 4589-2: 1996/Amd.1:2005

Specimen: Type III
Specimen thickness: 3.2mm
Ignition procedure: Method A

32.8%

16

Horizontal burning test

UL 94-2013 Section 7

Specimen: 126×13.4×3.0mm
Conditioning: 23±2℃
50±5%RH,48h

HB

17

20mm Vertiacal burning test

UL 94-2013 Section 8

Specimen: 126×13.4×3.0mm

V-1

18

Burning test

DIN 4102-1:1998-05

See appendix1

The sample tested met the requirements of class B2