| Brand | Impression |
|---|---|
| Color | Milky |
Wall Panel is made of PVC resin and cooperates with the professional formula. Put the PVC wall panel in acid-base salt solution for 24 hours, no reaction occurs, the PVC wall panel has excellent anti-corrosion performance
PVC Wall panel is produced according to the most scientific formula, with sufficient tensile strength and toughness, and the surface of PVC sheet is not easy to wear, which improves the scratch resistance of PVC Wall panel sheet.
PVC Wall panel is waterproof, dense, non-leakage, does not absorb moisture, so you don’t have to worry about moisture spills or wet walls.
UPVC Wall Panel only requires light mopping with mild detergent, and it is good to go.
There are lots of designs and colors for the ROOF Wall Panel, suitable for different kind of the constructions.
Width: 1130mm
Effecived width: 1080mm
Length: Customized
Thickness: 1.2mm, 1.5mm, 2.0mm, 2.5mm, 3.0mm
Application: Large-scale steel structure projects such as sheds, Factories, Warehouses, Markets, Farms, Farms, etc.
At present, UPVC Roof Sheet Trapezium T1130 is one of our products with the largest export volume, mainly for large-scale steel structure engineering projects, such as pig farms, cattle farms, chicken farms and other farms, and fertilizer plants, dyeing plants, electroplating, Plants for chemical products such as metal smelting, and some life scenes such as carports, etc.
Num. | Test Item | Test Method | The Test Condition | Test Result |
| 1 | Tensile strength | ISO 527-1:2012 & ISO 527 -2:2012 | Testing speed: 50mm/min | 23.1 Mpa |
| 2 | Flexural strength | ISO 178:2010/Amd.1:2013 Method A | Test speed: 1mm/min | 50.9 Mpa |
| 3 | Impact Resistance | With reference to GB/T 8814-2004 Section 5.7, Section 6.7 and client’s requirement | -10°C, 1h | Number of specimen failures: 0 |
| 4 | Vicat Softening Temperature | ISO 306:2013 Method B 50 | Rate of temperature: 50K/h | 77.0°C |
| 5 | Effects of liquid chemicals | ISO 175:2010 | Temperature: 23°C | No visual change |
ISO 175:2010 | Temperature: 23°C | Visual discoloring, but no other visual change | ||
ISO 175:2010 | Temperature: 23°C | No visual change | ||
| 6 | Light Ageing Test – Xenon-arc Exposure | ISO 4892-2:2013 cycle 4 & ISO 105-A02:1993/Cor.2:2005 & ASTM D2244– 15a | Exposure period: 1000h | Grey scale: 3 |
| 7 | Dimensional Stability | With reference to ASTM D1204-14 and client’s requirement | 100℃,60min→23±2℃, 50±5% RH, 60min | Direction of arrow: -0.6% |